Type: | Bare |
---|---|
Conductor Type: | Solid |
Application: | Heating |
Conductor Material: | Fecral |
Insulation Material: | Bare |
Material Shape: | Round Wire |
Leveranciers met geverifieerde zakelijke licenties
Merknaam | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr270Al7Mo2 | |
Belangrijkste chemische samenstelling% | CR | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
RE | opportuun bedrag |
opportuun bedrag |
opportuun bedrag |
opportuun bedrag |
opportuun bedrag |
opportuun bedrag |
opportuun bedrag |
|
FE | Rust | Rust | Rust | Rust | Rust | Rust | Rust | |
Nb0.5 | Mo1.8-2.2 | |||||||
Max. Continu servicetemperatuur van Element (ºC) |
950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
Weerstand Μm,20ºC |
1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
Dichtheid (g/cm3 ) |
7.4 | 7.10 | 7.16 | 7.25 | 7.35 | 7.10 | 7.10 | |
Thermisch geleidbaarheid KJ/m. |
52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
Coëfficiënt van expansie van leidingen Α×10-6/ºC |
15.4 | 16.0 | 14.7 | 15.0 | 13.5 | 16.0 | 16.0 | |
Smeltpunt ºC | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
Treksterkte MPa |
580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
Verlenging bij breuk % |
>16 | >12 | >12 | >12 | >12 | >12 | >10 | |
Variatie van oppervlakte % |
65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
Herhaal het buigen Frequentie (F/R) |
>5 | >5 | >5 | >5 | >5 | >5 | >5 | |
Hardheid (H.b.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
Micrografisch structuur |
Ferriet | Ferriet | Ferriet | Ferriet | Ferriet | Ferriet | Ferriet | |
Magnetisch eigenschappen |
Magnetisch | Magnetisch | Magnetisch | Magnetisch | Magnetisch | Magnetisch | Magnetisch |