Type: | TIG/MIG |
---|---|
Material: | Copper / Copper Alloy |
Flux Containing: | Not Containing Flux |
Slag Characteristic: | Acidic |
Extended Length: | >20mm |
Transportpakket: | 1kg/5kg/10kg/15kg |
Leveranciers met geverifieerde zakelijke licenties
Fosforbrons | |||||||||||||
CHEMISCHE SAMENSTELLING (%) | |||||||||||||
Standaard | Klasse | Legering | Cu | Al | FE | MN | Ni | P | PB | SI | SN | Zn | Overig |
ISO24373 | Cu5210 | CuSn8P | bal. | - | 0.1 | - | 0.2 |
0.01~ 0.4 |
0.02 | - |
7.5~ 8.5 |
0.2 | 0.2 |
GB/T9460 | SCu5210 | CuSn8P | bal. |
- |
max 0.1 |
- |
max 0.2 |
0.01~
0.4 |
max 0.02 |
- |
7.5~ 8.5 |
max 0.2 |
max 0.2 |
BS EN14640 | Cu5210 | CuSn9P | bal. | - | 0.1 | - | - |
0.01~ 0.4 |
0.02 | - |
7.5~ 9.0 |
0.2 | 0.5 |
AWS A5.7 | C52100 | Ercusn-C. | bal. | 0.01 | 0.10 | - | - |
0.10~ 0.35 |
0.02 | - |
7.5~ 9.0 |
0.2 |
0.50 |
Fysieke eigenschappen en mechanische eigenschappen: | |||||||||||||
Vaste-temperatuur | 875 ºC | Vloeistoffen-temperatuur | 1025 ºC | ||||||||||
Dichtheid | 8,8 kg/dm3 | Treksterkte | 260 N/mm2 | ||||||||||
Verlenging | 20% | Brinell hardheid | 80 HB | ||||||||||
Inleiding: | |||||||||||||
Aanbevolen voor het lassen van koper met Cu-Sn-legering.Best voor het lassen van messing met staal.Voorverwarming aanbevolen voor de grote maat Producten,en gepulseerd argon booglassen wordt aanbevolen voor meerlaagse hardvlakken op staal. |
HANDELSMERK | S213 |
Equivalent aan AWS | Ercusn-C. |
Kenmerken | Goede mechanische eigenschappen
Goede corrosiebestendigheid
|
Lasmethode | GTAW
Argon-booglassen
|
Toepassing | Gebruikt voor TIG, uitstekend voor gewoon of gecoat staal. Ook gebruikt voor het verven van arealen die worden blootgesteld aan corrosie. |
Fysieke eigenschappen en mechanische eigenschappen: | |
Vaste stoffen-temperatuur | 875 ºC |
Vloeistoffen-temperatuur | 1025 ºC |
Dichtheid | 8,8 kg/dm3 |
Treksterkte | 260 N/mm2 |
Verlenging | 20% |
Brinell hardheid | 80 HB |