Application: | Aviation, Electronics, Industrial, Medical, Chemical |
---|---|
Standard: | JIS, GB, DIN, BS, ASTM, AISI |
Purity: | 30% |
Alloy: | Alloy |
Type: | Resistance Alloy |
Powder: | Not Powder |
Leveranciers met geverifieerde zakelijke licenties
C | P | S | MN | SI | CR | Ni | Al | FE | Overig |
Max | |||||||||
0.08 | 0.02 | 0.015 | 0.60 | 0.75-1.60 | 18.0-22.0 | 30.0-34.0 | Max. 0.50 | Bal. | - |
Opbrengststerkte | Treksterkte | Verlenging |
MPa | MPa | % |
370 | 750 | 35 |
20 ºC | 100 ºC | 200°C. | 300 ºC | 400 ºC | 500 ºC | 600 ºC |
1 | 1.011 | 1.024 | 1.038 | 1.052 | 1.064 | 1.069 |
700 ºC | 800 ºC | 900 ºC | 1000 ºC | 1100 ºC | 1200 ºC | 1300 ºC |
1.073 | 1.078 | 1.088 | 1.095 | 1.109 | - | - |
Draad | 0,018 mm-10 mm |
Lint | 0.05*0,2 mm-2.0*6,0 mm |
Strip | 0.5*5,0 mm-5.0*250 mm |
Bar | 10 mm |
Producten | Afmetingen (mm) | Hoofdsamenstelling (%) | Toepassingen | |||
Ni | MN | SI | CR | |||
Ni-Mn-Si-CR (platte draad) | Dikte 1.0-2.0 Breedte 2.0-3.5 | bal. | 1.3-1.8 | 0.4-0.65 | 1.4-1.8 | geschikt voor het maken van een elektrode aan de zijkant voor de bougie |
Ni-Mn-Si-CR (ronde draad) | φ4.0-φ5.0 | bal. | 1.3-1.8 | 0.4-0.65 | 1.4-1.8 | geschikt voor het maken van centrale elektrode voor bougie |
Ni-CR-Mn-Si (ronde draad) | φ1.0-φ6.0 | bal. | 2.5-3.5 | 1.5-2.0 | 4.5-5.5 | geschikt voor het maken van centrale elektrode voor bougie |
Ni-Mn5 (ronde draad) | φ1.0-φ6.0 | bal. | 4.5-5.5 | geschikt voor het maken van centrale elektrode voor bougie en lood | ||
Cr20Ni30 | φ1.0-φ6.0 | 30-34 | FE(bal) | 1-2 | 18-22 | geschikt voor het maken van centrale elektrode voor bougie |
Producten | Treksterkte (N/mm2) | Verlenging(%) | Weerstand ( mm2/m) | Hardheid (HVO.2) |
Ni-Mn-Si-CR (platte draad) | ≥430 | ≥30 | 0.2-0.3 | ≤150 |
Ni-Mn-Si-CR (ronde draad) | ≥650 | ≥10 | 0.2-0.3 | ≤200 |
Ni-CR-Mn-Si (ronde draad) | ≥700 | - | 0.55-0.68 | ≤220 |
Ni-Mn5 (ronde draad) | ≥700 | ≥10 | 0.17-0.22 | ≤250 |