Processing Object: | Metal |
---|---|
Molding Style: | Forging |
Molding Technics: | Forging |
Application: | Machinery Parts |
Material: | SS |
Heat Treatment: | Quenching |
Leveranciers met geverifieerde zakelijke licenties
Legering |
% |
C |
CR |
Ni |
TI |
FE |
Cu |
MN |
SI |
75 |
Min. |
0.08 |
18 |
Balans |
0.2 |
||||
Max |
0.15 |
21 |
0.6 |
0.5 |
0.5 |
1 |
1 |
Dichtheid |
8.37 g/cm3 |
Smeltpunt |
2450-2520°C. |
Legering |
Treksterkte |
Warmtegeleiding |
Coëfficiënt van thermische uitzetting |
Hardheid HALFPENSION |
RM N/mm2 |
W/m? °C |
Μm/m/°C. |
||
Nimonic 75 (oplossing) |
1400-2210 |
11.7 |
11 |
241 |
Staaf, staaf, draad en smeedmateriaal |
BS HR 5, BS HR 504, DIN 17752, AECMA PREN2306, AECMA PREN2307, AECMA PrEN2306, AECMA Pr EN2307, AECMA Pren2402, ISO 9723, ISO 9724, ISO 9725 |
Plaat, vel, strook |
BS HR 203, DIN 17750, AECMA Pren2293, AECMA Pren2302, AECMA Pren2411, ISO 6208 |
Pijp en buis |
BS HR 403, DIN 17751, AECMA PREN2294, ISO 6207 |
Overig |
DIN 17742, AECMA Pren2308, Werkstoff nr. 2.4630, W. Nr 2.4951, UNS N06075, Nimonic 75 (handelsnaam), MSRR 7104 en MSRR 7004, AFNOR NC 20T |
Breeksterkte (1000 u) |
||
Temperatuur |
psi |
MPa |
760 °C / 1400 °F |
6000 |
40 |
815 °C / 1500 °F |
3500 |
24 |
870 °C / 1600 °F |
2200 |
15 |
925 °C / 1700 °F |
1500 |
10 |
980 °C / 1800 °F |
1200 |
8 |