Multi Layer Fiberglass Fabric

• Surface Treatment: No Coating
• Weave Type: Plain Woven
• Fiberglass Type: E-Glass
• Alkali Content: Alkali Free
• gewicht van de oppervlakte: 0.86 kg/m2
• rolbreedte: 1270 mm
• Transportpakket: in Pallet
• Specificatie: 3-60MM
• Handelsmerk: JLON
• Oorsprong: China
• Gs-Code: 70194000
• Productiecapaciteit: 200000m2

Beschrijving

Fiberglass 3D spacer fabric Introduction:
Fiberglass 3D spacer fabric is consist of two bi-direnctional woven fabric surfaces, which are mechanically connected with vertical woven piles. And two s-shape piles combine to form a pillar, 8 shape in warp and 1 shape in weft direction.It has broad application prospects in transportation, construction, petrochemical, aerospace, shipbuilding, wind energy and other fields.. 

Features and Advantages:

Glass fiber , carbon fiber, basalt fiber for option.
Design of structure parameters including areal density, height and distribution density of the pillars are all flexible.
It provide high skin-core debonding resistence and impact resistence with light weight, high stiffness,excellent thermal insulation,acoustic damping etc.

Specifications: 

Pilla Height		mm	3.0	4.0	5.0	6.0	8.0	10.0	12.0	15.0	20.0
Warp Density		ends/10cm	80	80	80	80	80	80	80	80	80
Weft Density		ends/10cm	96	96	96	96	96	96	96	96	96
Face Density	3D Spacer Fabric	kg/m2	0.86	0.96	1.01	1.08	1.12	1.24	1.37	1.52	1.72
	Sandwich construction	kg/m2	1.66	1.88	1.99	2.05	2.18	2.45	2.64	2.85	3.16
Flatwise Tensile Strength		Mpa	8.2	7.5	7.3	7.0	5.1	4.0	3.2	2.1	0.9
Flatwise Compressive Strength		Mpa	9.2	8.2	7.5	7.3	3.8	3.3	2.5	2.0	1.2
Flatwise Compressive Modulus		Mpa	25.0	27.4	43.1	41.1	32.5	43.4	35.1	30.1	26.3
Shear Strength	Warp	Mpa	3.1	2.9	2.7	2.5	1.3	0.9	0.8	0.6	0.3
	Weft	Mpa	6.5	6.0	4.3	4.1	2.3	1.5	1.3	1.1	0.9
Shear Modulus	Warp	Mpa	7.8	7.2	7.1	6.9	5.4	4.3	2.6	2.1	1.6
	Weft	Mpa	9.8	9.0	8.9	8.7	8.5	7.8	4.7	4.2	3.1
Bending Stiffness	Warp	N.m2	0.9	1.1	1.8	1.9	3.3	9.5	13.5	21.3	32.0
	Weft	N.m2	2.6	2.8	4.8	4.9	8.1	14.2	18.2	26.1	55.8