Usage: | General Plastics |
---|---|
Plastic Properties After Heated: | Thermoplastic Plastics |
Plastic Forming Method: | Injection |
verhouding: | 120-200% |
Glossiness: | glanzend |
toepassing: | Widely Used to Produce Slippers, Shoes |
Leveranciers met geverifieerde zakelijke licenties
EVA16%
|
|||
EIGENSCHAPPEN
|
TESTMETHODE
|
EENHEID
|
Gegevens
|
VA-gehalte
|
|
%
|
16
|
Dichtheid
|
ASTM D1505
|
g/cm3
|
0.937
|
Smeltindex MI2.16
|
ASTM D1238
|
g/10 min.
|
1.5
|
Treksterkte (breuk)
|
ASTM D638
|
Kg/cm2
|
170
|
Verlenging bij breuk
|
ASTM D638
|
%
|
700
|
Smeltpunt
|
ASTM D-3418
|
C
|
89
|
Hardheid
|
ASTM D2240
|
Wal D
|
37
|
EVA 18%
|
|
||
Eigenschappen
|
Testmethode
|
Waarde
|
|
VA-gehalte (%)
|
USI
|
18
|
|
Dichtheid (g/cm3)
|
ASTM D792
|
0.939
|
|
Smeltindex (g/10 min)
|
ASTM D1238
|
2.5
|
|
Treksterkte (gegoten)(breuk)(kg/cm2)
|
ASTM D638
|
180
|
|
Ultieme verlenging (gegoten)(%)
|
ASTM D638
|
750
|
|
Lage temperatuur-britleness (ºC/F50)
|
ASTM D746
|
<- 76
|
|
Vicat-verzachtingspunt (ºC)
|
ASTM D1525
|
64
|
|
Smeltpunt (ºC)
|
ASTM D3418
|
86
|
|
Hardheid (Shore D)
|
ASTM D2240
|
36
|
|
EVA28%
|
|
||
EIGENSCHAPPEN
|
TESTMETHODE
|
EENHEID
|
Gegevens
|
VA-gehalte
|
|
%
|
28
|
Dichtheid
|
ASTM D1505
|
g/cm3
|
0.954
|
Smeltindex MI2.16
|
ASTM D1238
|
g/10 min.
|
15
|
Treksterkte (breuk)
|
ASTM D638
|
Kg/cm2
|
80
|
Verlenging bij breuk
|
ASTM D638
|
%
|
>800
|
Smeltpunt
|
ASTM D-3418
|
C
|
69
|
Hardheid
|
ASTM D2240
|
Wal D
|
20
|
Voordeel:
Onze goederen hebben een uitstekende kwaliteit en een concurrerende prijs.
2.onze comapny-export van EVA-materialen voor meer dan 18 jaar.
Inhoud van VA
|
Toepassingsbereik
|
<5%
|
Film, draad en kabel, LDPE-modificatiemiddel, lijm, etc.
|
5%~10%
|
Elastische film, spuitgieten en schuimproducten, enz.
|
20% ~ 28%
|
Voornamelijk gebruikt voor hetelijmen en coatingproducten
|
28% - 33%.
|
Fotovoltaïsche materialen, zonnecellijmen, enz.
|
38% - 40%
|
Lijm
|