NL 3Cr17+S | JIS SUS420F | DIN 1.2085 Plastic Mold Staal
Land | China | Japan | Duitsland | VS | VK |
Standaard | GB/T 1299 | JIS G4404 | DIN EN ISO4957 | ASTM A681 | BS 4659 |
Kwaliteit | 3Cr17+S | SUS420F | 1.2085 | / | / |
Kwaliteit | C | SI | MN | P | S | CR | MA | Ni |
SUS420F | 0.26 - 0.4 | ≤1.00 | Max. 1.25 | Max. 0.06 | Max. 0.15 | 12.0-14.0 | Max. 0.6 | Max. 0.6 |
1.2085 | 0.28-0.38 | ≤1.00 | Max. 1.40 | Max. 0.03 | Max. 0.03 | 15.0-17.0 | / | Max. 1.0 |
Grootte | Rond | Dia 6-1200 mm |
Plaat/vlak/blok | Dikte 6 mm-500 mm |
|
Breedte 20 mm-1000 mm |
||
Proces | EAF+LF+VD+Forged+Heat Treatment (optioneel) | |
Warmtebehandeling | Genormaliseerd ; genormaliseerd ; getemperd ; getemperd | |
Staat van het oppervlak | Zwart; geschild; gepolijst; machinaal bewerkt; geslepen; Gedraaid; gefreesd | |
Leveringsconditie | Gesmeed; warm gewalst; koud getrokken | |
Test | Treksterkte, opbrengststerkte, verlenging, oppervlakte van de reductie, waarde van de impact, Hardheid, korrelgrootte, ultrasone test, inspectie in de VS, testen van magnetische deeltjes, enz. | |
Betalingsvoorwaarden | T/T;L/C;/Money gram/ Paypal | |
Handelsvoorwaarden | FOB; CIF; C&F; ENZ. | |
Levertijd | 30-45 dagen | |
Toepassing | DIN 1.2085 is van toepassing op alle soorten snijgereedschappen - matrijzen en matrijzen in de kunststoffenindustrie, zoals PVC, messen, scharen, chirurgische instrumenten, matrijzen voor de productie van kunststoffen, alsmede op chirurgische instrumenten en het meten van gauges.plates voor corrosiebestendige matrijsokkels en matrijssets; matrijzen voor corrosieve kunststoffen; de kosten voor bescherming en verzorging van matrijsgereedschappen worden verminderd dankzij de verhoogde corrosiebestendigheid; niet geschikt voor matrijswisselplaten. |
6:WARMTEBEHANDELING:
Gewoonlijk is geen warmtebehandeling vereist
Zacht uitgloeien:
850 tot 880 °C gedurende ongeveer 2 tot 5 uur
langzame gecontroleerde koeling, verdere koeling in lucht, verwateringshardheid max. 240 HB
Verharding:
1000 tot 1030 °C.
houd de uithardingstemperatuur 30 minuten
het is de voorkeur om in olie te kruipen
Haalbare hardheid: 48 HRC
Temperen:
langzame verwarming tot temperatuur onmiddellijk na het uitharden;
minimumtijd in de oven: 2 uur per 20 mm dikte van het onderdeel;
het is raadzaam om twee keer te temperen
7: Leveringsconditie
Bij warmgewalste platen is de leveringstoestand gewoonlijk warm gewalst, gegloeid, zwart oppervlak.
GB GB/T 1299 |
JIS JIS G4404 |
DIN (W-nr.) DIN EN ISO4957 |
AISI/ASTM ASTM A681 |
BS BS 4659 |
Gereedschap voor koud werk, staal | ||||
Cr12 | SKD1 | 1.2080/X210Cr12 | D3 | |
Cr5Mo1V | SKD12 | 1.2363/X100CrMoV5 | A2/T30102 | BA2 |
Cr12MoV | 1.2601 | D5 | ||
Cr12Mo1V1 | SKD11 | 1.2379/X153CrMo12 | D2 | |
X210CrW12 | SKD2 | 1.2436 | D6 | |
9CrWMn | SKS3 | 1.2510/100MnCrW4 | O1 | |
9 Mn2V | 1.2842 / 90MnCrV8 | O2 | B02 | |
5CrNiMo | SKT4 | 1.2713 | L6/T61206 | BH224/5 |
Gereedschap voor brandgevaarlijke werkzaamheden, staal | ||||
1.2355/50CrMoV13-15 | S7/T41907 | |||
5CrNiMoV | 1.2714 | 6F3 | ||
5CrNi4Mo | 1.2767 | 6F7 | ||
SKD7 | 1.2365/32CrMoV12-28 | H10/T20810 | BH10 | |
4Cr5MoV | SKD6 | 1.2343/X37CrMoV5-1 | H11/T20811 | BH11 |
4Cr5MoSiV1 | SKD61 | 1.2344/X40CrMoV5-1 | H13 | |
SKD62 | 1.2605/X35CrWMoV5 | H12/T20812 | BH12 | |
3Cr2W8V | SKD5 | 1.2581 | H21 | |
Kunststof matrijstaal | ||||
3Cr2Mo | 1.2311 | P20 | ||
NAK80 | 1.2312 | P20+S/ P21 | ||
3Cr2MnNiMo | 1.2738 | P20+Ni / 718 | ||
4Cr13 | SUS420J2 | 1.2083 | 415 | |
3Cr17+S | SUS420F | 1.2085 | ||
3Cr17Mo | SUS420J | 1.2316 | ||
Engineering Staal | ||||
GB GB/T 699 |
JIS JIS G4051 |
DIN (W-nr.) NL 10083-2 |
AISI/ASTM ASTM A20 |
EN/ BS |
1018 | EN2C | |||
20 | S20C | C20/1.1151 | 1020 | EN3B/070M20 |
S35C | C35 | 1035 | ||
1040 | EN8/080M40 | |||
45 | S45C | C45/1.1191 | 1045 | EN8D/C45E |
50 | S50C | 1050 | ||
S55C | 1055 | EN9/070M55 | ||
V345 | S355/ST52-3/1.1170 | EN14/150M19 | ||
GB GB/T 3077 |
JIS JIS G4105/JIS G4103 |
DIN (W-nr.) NL 10250 |
AISI/ASTM ASTM A29 |
BS BS 970 |
40 Cr | SCr440 | 41Cr4(1.7035) | 5140 | |
SCM420 | 1.7243 | 4118 | ||
30CrMo | SCM430 | 25CrMo4/1.7218 | 4130 | 708A25/708M25 |
42 CrMo | SCM440 | 42crmo4/1.7225 | 4140 | EN19/709M40 |
4145 | ||||
4330 | ||||
40CrNiMoA | SNCM 439/SNCM8 | 36CrNiMo4/1.6511 | 4340 | EN24/817M40 |
1.6745-5-11 | EN 26 | |||
34CrNiMo6 / 1.6582 | 4337 | |||
30CrNiMo16-6/1.6747 | EN30B/835M30 | |||
1.7361 | EN40B/722M24 | |||
SCM415 | 16MnCr5 / 1.7131 | 5115 | ||
15CrNi6/1.5919 | 3115 | |||
1.5714 | EN351/635M15 | |||
4615/4617 | EN34/665M17 | |||
1.5752 | 3310/3415 | EN36/655M13 | ||
15NiCrMo16-5/1.6723 | EN39/835M15 | |||
18CrNiMo7-6 (1.6587) | 4815 | |||
SNCM220 | 1.6523/21NiCrMo2 | 8620 | 805M20 | |
20CrNiMo5 | EN353 | |||
GCr15 | 52100/1.3505 | EN31/535A99 | ||
Roestvrij staal | ||||
SUS440C | X105CrMo17/1.4125 | S44004/440C | ||
Slijtvast staal | ||||
GB | JIS | DIN (W-nr.) | AISI/ASTM | SSAB |
NM400 | HB400 | |||
NM500 | HB500 | |||
Veerstaal | ||||
GB | JIS | DIN (W-nr.) | AISI/ASTM | SSAB |
65 MN | 1066 | |||
60Si2Mn | SUP6 | 60Si7 | 9260 | |
60Si2MnA | SUP7 | 60Si7 | 9260 | |
55 CrMnA | SUP9 | 55 Cr3 | 5155 | |
60CrMnA | SUP9A | 5160 | ||
50 kVA | SUP10 | 51CrV4 | 6150 | |
Staal met hoge snelheid | ||||
GB | JIS JIS G4403 |
DIN (W-nr.) DIN EN ISO 4957 |
AISI/ASTM ASTM A600 |
BS BS 4659 |
SKH51 | 1.3343 | M2 | ||
SKH55 | 1.3243/HS6-5-2-5 | M35 | ||
SKH59 | 1.3247/HS2-9-1-8 | M42 | ||
SKH2 | HS18-0-1-1.3355 | T1 | ||
SKH3 | S 18-1-2-5/1.3255 | T4/T12004 | ||
SKH4 | 1.3265/S18-1-2-10 | T5/T12005 | BT5 | |
Alle soorten smeedstukken volgens tekening |
Grootte | Rond | Dia 8-1200 mm |
Plaat/vlak/blok | Dikte 10mm-800mm |
|
Breedte 20 mm-2000 mm |
||
Warmtebehandeling | Genormaliseerd ; genormaliseerd ; getemperd ; getemperd | |
Staat van het oppervlak | Zwart; geschild; gepolijst; machinaal bewerkt; geslepen; Gedraaid; gefreesd | |
Leveringsconditie | Gesmeed; warm gewalst; koud getrokken | |
Test | Treksterkte, opbrengststerkte, verlenging, oppervlakte van de reductie, waarde van de impact, Hardheid, korrelgrootte, ultrasone test, inspectie in de VS, testen van magnetische deeltjes, enz. | |