Type: | Round |
---|---|
Standard: | AISI, ASTM, DIN, JIS, GB, BS |
Composition: | Stainless Steel Scrap |
Technique: | Forged |
Shape: | Plate |
Surface Treatment: | Polished |
Leveranciers met geverifieerde zakelijke licenties
C | SI | MN | P | S | CR | MA | W | V | CO | Ni |
---|---|---|---|---|---|---|---|---|---|---|
1,50-1,80 | 0,15-0,40 | 0,15-0,45 | Max. 0,030 | Max. 0,030 | 11,00-13,00 | - | - | - | - | - |
Hardheid na | Temperen ºC | Symbool | Waarde |
Zacht annealing | - | HALFPENSION | ≤255 |
Afzetten met 960 ºC in olie | - | HRC | 63.5 |
Afkoeling met 960 ºC in olie en temperen | 180 | HRC | ≥62 |
200 | HRC | 61.5 | |
250 | HRC | 59.5 | |
300 | HRC | 58 | |
350 | HRC | 57 | |
400 | HRC | 55.5 | |
450 | HRC | 55 |
Technologische behandelingsprocessen | Mogelijke toepassing | Temperatuur, °C. | ||
Hete vorming | Smeden | + | 1050-850 | |
Rollen | + | 1050-850 | ||
Behandeling | Warmtebehandeling | Afdrenken | + | 980-1000 |
Temperen | + | 220-450 | ||
Versterking van de neerslag | Supersaturatie | - | - | |
Veroudering | - | - | ||
Uitgloeien | Zacht annealing | + | 820-860 | |
Spanningsloos maken | + | 600-700 | ||
Thermochemische behandeling | Nitriden | - | - | |
Overig | - | - |