Techniek: | Hot-Rolled+Cold-Drawn |
---|---|
Oppervlakte Behandeling: | as Required |
snijservice: | beschikbaar |
mtc: | 3.1 of 3.2 certificaat |
Transportpakket: | Seaworthy Standard Package |
Specificatie: | 30-850mm |
Leveranciers met geverifieerde zakelijke licenties
Specificaties : | ASTM A213 / ASME SA213 |
Materiaalsoort : | T2, T5, T9, T11, T12, T17, T21, T22, T23, T24, T91, T92, T122, T911, 304, 304L/H, 304LN, 309H, 310/S/H, 316, 316 LINKS, 316 TI, 317, 317 L, 321/H, 347/H 410, 446, 904L |
Type leverancier | NAADLOOS / GELAST / ERW / EFW / KOUD TREKKEN / WARME AFWERKING / KOUDE AFWERKING |
Grootte : | 1/4" BUITENDIAMETER, NB TOT 3" BUITENDIAMETER, NB MATEN NAADLOOS - 6 MM BUITENDIAMETER TOT 114.3 MM BUITENDIAMETER GELAST / ERW- 10 MM TOT 114.3 MM BUITENDIAMETER |
Dikte : | 1 mm tot 12 mm, SCH 5/5S, 10/10S, 20/20S, 40/40S, 80/80S, 120/120S, 160/160S volgens ANSI B36.19/36.10 |
Lengte : | 01 meter tot 12.5 meter, enkele willekeurige lengte, dubbele willekeurige lengte en grootte aanpassen. |
Leveringsvoorwaarden | Zoals gerold, gevormd, spanningsarm, gegloeid, gehard, Getemperd, koude afname |
Voltooien : | Electropolak, Mechanische Pools, Satijn afwerking, gepassiveerd |
Einde : | Normaal uiteinde, afgeschuind uiteinde |
Overige tests | Productanalyse, transversale spanningstest, afvlaktest, Etstest, radiografisch onderzoek, Stabiliserende warmtebehandeling, Intergranulaire corrosietest, test van lasverval, detectie van magnetische deeltjes, Test van korrelgrootte, NACE 0175, Dual Grade, PWHT (NABEHANDELING VAN LASWARMTE), flare-test, Bend-test, Hardheid-test, Tensile-test, enz. |
Afmeting | Alle leidingen worden vervaardigd en geïnspecteerd/ getest naar de Relevante standaarden, waaronder ASTM en ASME |
Diensten met toegevoegde waarde | Tekenen / uitzetting / Machining / zandstralen / shot Stralen / warmtebehandeling / Gegloeid / Gegloeid |
Verpakking | Los / Bundle / Houten Pallet / Houten doos / Plastic doekwikkelingen / kunststof einddoppen / afgeschuinde beschermer |
Verzending en transport | Over zee - Break-bulk conventioneel schip / FCL (Full Container Load) / LCL (less Container Load) / 20 feet container / 40 feet container / 45 feet container / High Cube container / Open Top container, by Air - Freighter Civil Passenger and Cargo Planes |
Certificaat materiaaltest | Testcertificaat van de fabrikant volgens EN10204 3.1, 3.2 / Laboratoriumtestcertificaat van het door NABL goedgekeurde laboratorium. / onder Inspectie-bureau van derden zoals SGS, TUV, DNV, LLOYDS, ABS ETC |
Kwaliteit | C | SI | MN | P, S Max | CR | MA | Max. Ni | V | Al Max | W | B | NB | N | T. S. | Y. P | Verlenging | Hardheid |
T2 | 0.10-0.20 | 0.10-0.30 | 0.30-0.61 | 0.025 | 0.50-0.81 | 0.44-0.65 | - | - | - | - | - | - | - | ≥ 415 MPa | ≥ 205 MPa | ≥ 30% | 163 HBW (85 HRB) |
T5 | MAX. 0.15 | MAX. 0.50 | 0.30-0.60 | 0.025 | 4.00-6.00 | 0.45-0.65 | ≥ 415 MPa | ≥ 205 MPa | ≥ 30% | 163 HBW (85 HRB) | |||||||
T9 | MAX. 0.15 | 0.25-1.00 | 0.30-0.60 | 0.025 | 8.00-10.00 | 0.90-1.10 | ≥ 415 MPa | ≥ 205 MPa | ≥ 30% | 163 HBW (85 HRB) | |||||||
T11 | 0.05-0.15 | 0.50-1.00 | 0.30-0.60 | 0.025 | 1.00-1.50 | 0.44-0.65 | - | - | - | - | - | - | - | ≥ 415 MPa | ≥ 205 MPa | ≥ 30% | 163 HBW (85 HRB) |
T12 | 0.05-0.15 | Max. 0.5 | 0.30-0.61 | 0.025 | 0.80-1.25 | 0.44-0.65 | - | - | - | - | - | - | - | ≥ 415 MPa | ≥ 220 MPa | ≥ 30% | 163 HBW (85 HRB) |
T22 | 0.05-0.15 | Max. 0.5 | 0.30-0.60 | 0.025 | 1.90-2.60 | 0.87-1.13 | - | - | - | - | - | - | - | ≥ 415 MPa | ≥ 205 MPa | ≥ 30% | 163 HBW (85 HRB) |
T91 | 0.07-0.14 | 0.20-0.50 | 0.30-0.60 | 0.02 | 8.0-9.5 | 0.85-1.05 | 0.4 | 0.18-0.25 | 0.015 | - | - | 0.06-0.10 | 0.03-0.07 | ≥ 585 MPa | ≥ 415 MPa | ≥ 20% | 250 HBW (25 HRB) |
T92 | 0.07-0.13 | Max. 0.5 | 0.30-0.60 | 0.02 | 8.5-9.5 | 0.30-0.60 | 0.4 | 0.15-0.25 | 0.015 | 1.50-2.00 | 0.001-0.006 | 0.04-0.09 | 0.03-0.07 | ≥ 620 MPa | ≥ 440 MPa | ≥ 20% | 250 HBW (25 HRB) |
Staalsoorten | ASTM A213 Chemische samenstelling % Max | Staalsoorten | Warmtebehandeling | Temperatuur F (C) Min. | ASTM-GRAANGROOTTENUMMER | Treksterkte KSi (MPa), min. | Opbrengststerkte KSi (MPa), min. | Rek %, min. | Hardheid | |||||||||||
C | MN | P | S | SI | CR | Ni | MA | NB | NB | TI | Brinell | Rockwell | ||||||||
TP304 | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 18.0-20.0 | 8.0-11.0 | ... | ... | ... | ... | TP304 | Oplossing | 1900 (1040) | ... | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP304H | 0.04-0.10 | 2 | 0.04 | 0.03 | 0.75 | 18.0-20.0 | 8.0-11.0 | ... | ... | ... | ... | TP304L | Oplossing | 1900 (1040) | ... | 70(485) | 25(170) | 35 | 192 HBW/200HV | 90HRB |
TP304L | 0.035 | 2 | 0.04 | 0.03 | 0.75 | 18.0-20.0 | 8.0-13.0 | ... | ... | ... | ... | TP304H | Oplossing | 1900 (1040) | 7 | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP310S | 0.08 | 2 | 0.045 | 0.03 | 0.75 | 24.0-26.0 | 19.0-22.0 | 0.75 | ... | ... | ... | TP310S | Oplossing | 1900 (1040) | ... | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP310HCbN | 0.04-0.10 | 2 | 0.03 | 0.03 | 0.75 | 24.0-26.0 | 17.0-23.0 | ... | 0.15-0.35 | 0.20-0.60 | ... | TP310HCbN | Oplossing | 2000 (1110) | 7 | 95(655) | 43(295) | 30 | 256 HBW | 100 HRB |
TP316 | 0.08 | 2 | 0.04 | 0.03 | 0.75 | 16.0-18.0 | 11.0-14.0 | 2.00-3.00 | ... | ... | ... | TP316 | Oplossing | 1900 (1040) | ... | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP316L | 0.035 | 2 | 0.04 | 0.03 | 1 | 16.0-18.0 | 10.0-15.0 | 2.00-3.00 | ... | ... | ... | TP316L | Oplossing | 1900 (1040) | ... | 70(485) | 25(170) | 35 | 192 HBW/200HV | 90HRB |
TP316H | 0.04-0.10 | 2 | 0.04 | 0.03 | 0.75 | 16.0-18.0 | 11.0-14.0 | 2.00-3.00 | ... | ... | ... | TP316H | Oplossing | 1900 (1040) | 7 | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP321 | 0.08 | 2 | 0.04 | 0.03 | 0.75 | 17.0-20.0 | 9.0-13.0 | ... | ... | ... | 5C-0.60 | TP321 | Oplossing | 1900 (1040) | 7 | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP321H | 0.04-0.10 | 2 | 0.04 | 0.03 | 0.75 | 17.0-20.0 | 9.0-13.0 | ... | ... | ... | 4C-0.60 | TP321H | Oplossing | 2000(1100) | 7 | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP347 | 0.08 | 2 | 0.04 | 0.03 | 0.75 | 17.0-19.0 | 9.0-13.0 | ... | ... | 10xC-1.00 | ... | TP347 | Oplossing | 1900(1040) | ... | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
TP347H | 0.04-0.10 | 2 | 0.04 | 0.03 | 0.75 | 17.0-20.0 | 9.0-13.0 | ... | ... | 8xC-1.00 | ... | TP347H | Oplossing | 2000(1100) | 7 | 75(515) | 30(205) | 35 | 192 HBW/200HV | 90HRB |
Leveranciers met geverifieerde zakelijke licenties