Material: | Nylon |
---|---|
Applications: | Transportation Textiles |
Type: | Tyre Cord Fabric |
Style: | Dyed |
Pattern: | Plain |
Width: | 57/58" |
Leveranciers met geverifieerde zakelijke licenties
Item |
1870dtex/2 (1680D/2) |
1400dtex/2 1260D/2 |
930dtex/2 840D/2 |
2100 dtex/2 (1890d/2) |
1170dtex/1 (1050D/1) |
700 dtex/1 (630D/1) |
1870dtex/1 (1680D/1) |
1400dtex/1 (1260D/1) |
930dtex/1 (840D/1) |
||
Breeksterkte ≥ | N. V. T. | 279.30 | 215.60 | 137.20 | 313.60 | 90.00 | 50.00 | 137.00 | 107.00 | 70.00 | |
Verlenging Bij | 88, 2N | % | 9.5±0.5 | - | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - |
66, 6N | - | 9.5±0.5 | - | - | 8.0±0.8 | - | - | 7.0±0.8 | - | ||
44, 1N | - | - | 9.5±0.5 | - | - | 7.5±0.8 | - | - | 7.5±0.8 | ||
Kleefkracht ≥ | N. V. T. | 166.60 | 147.00 | 117.60 | 176.40 | 65.00 | 43.00 | 83.00 | 69.00 | 54.00 | |
Breaking Sterkte Verschil≤ | % | 3.80 | 3.80 | 3.80 | 3.80 | 5.00 | 5.00 | 5.00 | 5.00 | 5.00 | |
Het verschil In rek ≤ | 6.30 | 6.30 | 6.30 | 6.30 | 7.00 | 7.50 | 7.00 | 7.00 | 7.00 | ||
Dip Pick -up | 4.5±1.0 | 4.5±1.0 | 4.5±1.0 | 4.5±1.00 | 4.2±0.8 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | 4.2±1.00 | ||
Rek breken | % | 23.0±2.0 | 23.0±2.0 | 22.0±2.0 | 23±2.0 | 20.0±2.0 | 19.0±2.0 | 20.0±2.0 | 20.0±2.0 | 20.0±2.0 | |
Diameter | mm | 0.78±0.03 | 0.65±0.03 | 0.55±0.03 | 0.78±0.03 | - | 0.23±0.03 | 0.5±0.03 | 0.43±0.03 | 0.32±0.03 | |
Draai | Primaire Draaiing (Z) | Twist/m | 320±15 | 370±15 | 460±15 | 320±15 | Tpm/m: 200±15 | Tpm/m: 260±15 | 160±10 | 190±10 | 210±15 |
Tweede Draai(en) | 320±15 | 370±15 | 460±15 | 320±15 | |||||||
Krimp van de hitte ≤ | % | 6.00 | 6.00 | 6.00 | 4.00 | 4.50 | 4.00 | 4.00 | 4.00 | 4.00 | |
Vocht ≤ | % | 1.00 | 1.00 | 1.00 | 1.00 | 0.80 | 0.80 | 0.80 | 0.80 | 0.80 |
NEE | ITEMS | VERENIGEN | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
(1100 dtex/2) | (1440 dtex/2) | (1100 dtex/3) | (1670dtex/2) | (2200 dtex/2) | (1440 dtex/3) | (1670dtex/3) | ||||
1 | Breeklengte (min. ) | N. V. T. | 140 | 180 | 205 | 205 | 280 | 260 | 305 | |
2 | Verlenging Bij 44, 1N | % | 4.5+1.0 | |||||||
Verlenging Bij 58, 0N | % | 4.5+1.0 | ||||||||
Verlenging Bij 66.6N | % | 4.5+1.0 | 4.5+1.0 | |||||||
Verlenging Bij 88, 2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
Verlenging Bij 100N | % | 4.5+1.0 | ||||||||
3 | Adhensie (H-test) (min) | N. V. T. | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
4 | Verschil in breaking -sterkte (max. ) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
5 | Het verschil In verlenging Breken (max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
6 | Dip Pick -up | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
7 | Rek bij breuk (min. ) | % | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | 15+/-2 | |
8 | Diameter | mm | 0.56+0.03 | 0.61+0.03 | 0.66+0.03 | 0.66+0.03 | 0.75+0.03 | 0.74+0.03 | 0.81+0.03 | |
9 | Draai | Pingle Twist (Z) | T/10 cm. | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 |
Twist (S) van de ply | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 31+1.5 | |||
10 | Heteluchtkrimp 177 ºC × 2minx0, 05CN/dtex(max) | % | 3 | 3 | 3 | 3 | 3 | 3 | 3 | |
11 | Verlenging Bij Het breken Van Het inslaggaren (min. ) | % | 120 | 120 | 120 | 120 | 120 | 120 | 120 |
NEE | ITEMS | VERENIGEN | 1000D/2 | 1300D/2 | 1000D/3 | 1500D/2 | 2000D/2 | 1300D/3 | 1500D/3 | |
(1100 dtex/2) | (1440 dtex/2) | (1100 dtex/3) | (1670dtex/2) | (2200 dtex/2) | (1440 dtex/3) | (1670dtex/3) | ||||
1 | Breeklengte (min. ) | N. V. T. | 140 | 180 | 205 | 205 | 270 | 260 | 305 | |
2 | Verlenging Bij 44, 1N | % | 4.5+1.0 | |||||||
Verlenging Bij 58, 0N | 4.5+1.0 | |||||||||
Verlenging Bij 66.6N | 4.5+1.0 | 4.5+1.0 | ||||||||
Verlenging Bij 88, 2N | % | 4.5+1.0 | 4.5+1.0 | |||||||
Verlenging Bij 100N | % | 4.5+1.0 | ||||||||
3 | Adhensie (H-test) (min) | N. V. T. | 125 | 135 | 140 | 140 | 170 | 165 | 180 | |
4 | Verschil in breaking -sterkte (max. ) | % | 4 | 4 | 4 | 4 | 4 | 4 | 4 | |
5 | Het verschil In verlenging Breken (max) | % | 5 | 5 | 5 | 5 | 5 | 5 | 5 | |
6 | Dip Pick -up | % | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | 3.5+1 | |
7 | Rek bij breuk (min) | % | 14 | 14 | 14 | 14 | 14 | 14 | 14 | |
8 | Diameter | mm | 0.56+0.03 | 0.61+0.03 | 0.66+0.03 | 0.66+0.03 | 0.75+0.03 | 0.74+0.03 | 0.81+0.03 | |
9 | Draai | Pingle Twist (Z) | T/10 cm. | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 |
Twist (S) van de ply | 45+1.5 | 40+1.5 | 37+1.5 | 37+1.5 | 33+1.5 | 33+1.5 | 30+1.5 | |||
10 | Heteluchtkrimp 177 ºC × 2minx0, 05CN/dtex(max) | % | 2 | 2 | 2 | 2 | 2 | 2 | 2 | |