Type: | Welding Wire |
---|---|
Materiaal: | Nikkel / nikkel legering |
Flux bevattende: | Zonder Flux |
belangrijkste chemische samenstelling: | Ni, Mo, Cr, Fe |
voortgang van het lassen: | TIG/MIG |
verlenging: | 27% |
Leveranciers met geverifieerde zakelijke licenties
C |
SI |
MN |
S |
P |
Ni |
≤0.05 |
≤0.2 |
≤2.0 |
≤0.01 |
≤0.01 |
Rust |
CR |
TI |
FE |
Cu |
andere |
|
42-46 |
0.3-1.0 |
≤0.5 |
≤0.15 |
< 0.5 |
Proces |
Diameter |
Spanning |
Stroomsterkte |
Gas |
TIG |
0, 9 mm (035 inch) 045 inch (1, 2 mm) 1, 6 mm (1/16 inch) 2, 4 mm (3/32 inch) 3, 2 mm (1/8 inch ) |
12-15 13-16 14-18 15-20 15-20 |
60-90 80-110 90-130 120-175 150-220 |
100% Argon 100% Argon 100% Argon 100% Argon 100% Argon |
MIG |
0, 9 mm (035 inch) 045 inch (1, 2 mm) 1, 6 mm (1/16 inch) |
26-29 28-32 29-33 |
150-190 180-220 200-250 |
75% Argon + 25% Helium 75% Argon + 25% Helium 75% Argon + 25% Helium |
ZAAG |
2, 4 mm (3/32 inch) 3, 2 mm (1/8 inch ) 32 Mm (5/5") |
28-30 29-32 30-33 |
275-350 350-450 400-550 |
Er kan Een geschikte Flux worden gebruikt Er kan Een geschikte Flux worden gebruikt Er kan Een geschikte Flux worden gebruikt |
Treksterkte |
105, 000 PSI |
730 MPA |
Verlenging |
30% |