Standaard: | GB |
---|---|
Toepassing: | lader, Metallurgical Machinery, cement Plant, Mining Machine |
Materiaal: | Aluminium |
Type: | Slijtvaste keramische |
dichtheid: | 3.60-4.2 |
al2o3-inhoud: | 92%, 95%, 99%, zta |
Leveranciers met geverifieerde zakelijke licenties
92 | 95 | T95 | 99 | ZTA | ZrO2 | Teststandaard | |
Dichtheid (g/cm³) | ≥3.6 | ≥3.65 | ≥3.7 | ≥3.83 | ≥4.15 | ≥5.9 | GB/T 25995-2010 |
Al2O3(%) | ≥92% | ≥95% | ≥95% | ≥99% | ≥75% | / | JC/T 1085-2008 |
ZrO2 +Y2O3 | / | / | / | / | ≥21% | ≥99.8% | JC/T 1085-2008 |
Buigsterkte (MPa) | ≥220 | ≥250 | ≥300 | ≥330 | ≥400 | ≥800 | GB/T 6569-2006 |
Druksterkte (MPa) | ≥1050 | ≥1300 | ≥1600 | ≥1800 | ≥2000 | / | GB/T 8489-2006 |
Taaiheid breuk (MPa.m1/2) | ≥3.2 | ≥3.2 | ≥3.5 | ≥3.5 | ≥5.0 | ≥7.0 | ISO21618 IM |
Rockwell Hardheid HRA | ≥82 | ≥85 | ≥88 | ≥89 | ≥90 | ≥88 | GB/T 230.1-1996 |
Vickers hardheid HV20 (MPa) | ≥950 | ≥1000 | ≥1100 | ≥1200 | ≥1400 | ≥1100 | GB/T 16534-2009 |
Slijtagevolume (cm³) | ≤0.25 | ≤0.20 | ≤0.15 | ≤0.10 | ≤0.05 | ≤0.05 | JC/T2345-2015 |